ASA SYNTHETIC Roofing Resin Tile ROYAL 1050


Product Ihe

Ngwaahịa

Ngwaahịa nkọwa:

Njirimara

Agba agba
Ezigbo mgbochi ikike
Ezigbo mkpuchi ihe
Ihe magburu onwe ya
Ezigbo ujọ Nguzogide
Obere Oguzogide Okpomọkụ
Ezigbo nhicha onwe
Ezigbo mkpuchi ọkụ
Mbibi Ike
Ezigbo Nguzogide Mmiri
Ọkụ siri ike
Ezigbo mkpuchi
Nchedo Gburugburu
Ntinye ngwa ngwa


ASA ụlọ mpempe akwụkwọ Project

ASA Resin ụlọ Sheet Project

Sịntetik resin ụlọ mpempe akwụkwọ Project

Sịntetik resin ụlọ Project

ASA SYNTHETIC RESIN ROOF TILE NWERE ISI SGS

MBA. Ihe nnwale Usoro ule
1 Agba ịnọgidesi ike ISO4892-2: 2013, ISO105-A02: 199

3 Cor2: 2005 na ASTM

D2244-11

2 Muriatic acid na-eguzogide ISO175-2010
3 Sururic acid na-eguzogide ISO175-2010
4 Nguzogide Alkali ISO175-2010
5 Ike ọdụdọ ISO 527-1: 2012 na ISO527-2: 2012
6 Elu ọnụ tensile nje na ezumike ISO 527-1: 2012 na ISO527-2: 2012
7 Ike mgbanwe ISO 178: 2010 / Amd.1: 2013Azọ A
8 Nguzogide mmetụta GB / T 8814-2004 Nkebi5.7 na 6.7
9 Ndepụta Oxygen ISO 4589-1: 1996 na ISO4589-2: 1996 / Amd.1: 2005
10 Nnwale na-ere ọkụ DIN 4102-1: 1998-05

ASA SYNTHETIC RESIN ROOF ILLỌ AKA NT FROMTA SGS (2014)

MBA. Ihe nnwale Usoro ule Ọnọdụ ule
1 Ihe ngosi Xenon-arc ISO 4892-2: 2013, ISO 105-A02: 1993 

Cor2: 2005 na ASTM D2244-11

ISO 4892-2: 2013 okirikiri 4 Irradiance: (0.51 ± 0.02) W / (m2 · nm) @ 340nm 102min light at (63 ± 3) ℃ BPT, (50 ± 10) ℃ RH

18min ìhè na mmiri sparay Myọcha: Boro / Boro

Oge ikpughe: 500h

       
2 Ahụike na-eguzogide N'ihe banyere ASTM D3045-92 (2010) na ihe ndị ahịa chọrọ 150 ℃ .30min
3 Muriatic acid na-eguzogide N'ihe banyere ISO 175-2010 na ihe ndị ahịa chọrọ Ọkara: 35% (m / m) HCI (AR)

Usoro: Usoro imikpu

Okpomọkụ: Roomlọ okpomọkụ

Oge ule: 48h

4 Sururic acid na-eguzogide N'ihe banyere ISO 175-2010 na ihe ndị ahịa chọrọ Ọkara: 30% (m / m) H2SO4 (AR)

Usoro: Usoro imikpu

Okpomọkụ: Roomlọ okpomọkụ

Oge ule: 48h

5 Nguzogide Alikali N'ihe banyere ISO 175-2010 na ihe ndị ahịa chọrọ Ọkara: 40% (m / m) NaOH (AR)

Usoro: Usoro imikpu

Okpomọkụ: Roomlọ okpomọkụ

Oge ule: 48h

6 Njupụta ISO 1183-1: 2012 Azọ A Mmanya na-aba n'anya, 23 ± 0,5 ℃
7 Ike mgbanwe ISO 178: 2010 / Amd.1: 2013

Azọ A

Ngwaahịa : 100x10.96x3.12mm

Speedgba ọsọ: 1mm / min

Oge: 50mm

8 Mgbanwe mgbanwe    
9 Charpy enweghi ike imetuta mmetụta ISO 179-1: 2010 Kwadoro: ISO 179-1 / 1Eu

Mkpụrụ ọkpụrụkpụ: 3.13mm

Okpukpe nke ihe: 5J

Mmetụta ọsọ: 2.90m / s

Oge: 62mm

10 Vicat na-eme ka okpomọkụ dị jụụ ISO 306: 2004 Bzọ B50 Mkpụrụ ọkpụrụkpụ: 3.01mm

Ọnụego okpomọkụ: 50 ℃ / h

11 Ike ọdụdọ ISO 527-1: 2012 na ISO 527-2: 2012 Ihe nlele: Pịnye 1B

Mkpụrụ ọkpụrụkpụ: 3.05mm

Nnwale ule: 5mm / min

Adịgide nkewa: 115mm

12 Elu ọnụ tensile nje na ezumike    
13 Nguzogide mmetụta GB / T 8814-2004 Nkebi 5.7 na 6.7 Mkpebi: -10 , , 1h →

Wepụ ma nwalee n'ime 10s.

Mkpụrụ ọkpụrụkpụ: 3.02mm

Geometry: H.25

Ebu ibu: 1.0kg

Oge: 200mm

Ọnụ ọgụgụ nke ụdị a nwalere: 10

14 Akụkụ mgbanwe N'ihe banyere ASTM D1204-08 na ihe ndị ahịa chọrọ Ọnọdụ: 100 ℃ , 60min →

23 ± 2 ℃ , 50 ± 5% RH, 1h

Gbasara: 25x25cm

Ọkara: Talcum ntụ ntụ

       
15 Ndepụta Oxygen ISO 4589-1: 1996 na ISO 4589-2: 1996 / Amd.1: 2005 Ntinye: Typedị III

Mkpụrụ ọkpụrụkpụ: 3.2mm

Usoro mgbanye: Azọ A

16 Kwụ ọkụ ule UL 94-2013 Nkebi 7 Ntughari: 126x13.4x3.0mm

Ọnọdụ: 23 ± 2 ℃, 50 ± 5% RH, 48h

17 20mm Vertiacal na-agba ọkụ ule UL 94-2013 Nkebi 8 Ntughari: 126x13.4x3.0mm
18 Nnwale na-ere ọkụ DIN 4102-1: 1998-05 Lee mgbakwunye 1